Systems and apparatus for atomic-layer deposition

ABSTRACT

The present inventors devised unique atomic-layer deposition systems, methods, and apparatus suitable for aluminum-oxide deposition. One exemplary method entails providing an outer chamber enclosing a substrate, forming an inner chamber within the outer chamber, and introducing an oxidant into the inner chamber, and introducing an aluminum precursor into the inner chamber. The inner chamber has a smaller volume than the outer chamber, which ultimately requires less time to fill and purge and thus promises to reduce cycle times for deposition of materials, such as aluminum oxide.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a divisional of U.S. application Ser. No.10/137,168, filed May 2, 2002, which is incorporated herein by referencein its entirety.

TECHNICAL FIELD

This invention concerns methods of making integrated circuits,particularly layer formation techniques, such as chemical-vapordeposition and atomic-layer deposition.

BACKGROUND OF INVENTION

Integrated circuits, the key components in thousands of electronic andcomputer products, are interconnected networks of electrical componentsfabricated on a common foundation, or substrate. Fabricators generallybuild these circuits layer by layer, using techniques, such asdeposition, doping, masking, and etching, to form and interconnectthousands and even millions of microscopic transistors, resistors, andother electrical components on a silicon substrate, known as a wafer.

One common technique for forming layers in an integrated circuit iscalled chemical vapor deposition. Chemical vapor deposition generallyentails placing a substrate in a reaction chamber, heating the substrateto prescribed temperatures, and introducing one or more gases, known asprecursor gases, into the chamber to begin a deposition cycle. Theprecursor gases enter the chamber through a gas-distribution fixture,such as a gas ring or a showerhead, one or more centimeters above thesubstrate, and descend toward the heated substrate. The gases react witheach other and/or the heated substrate, blanketing its surface with alayer of material. An exhaust system then pumps gaseous by-products orleftovers from the reaction out of the chamber through a separate outletto complete the deposition cycle.

Conventional chemical-vapor-deposition (CVD) systems suffer from atleast two problems. First, conventional CVD systems generally formnon-uniformly thick layers that include microscopic hills and valleys,and thus generally require use of post-deposition planarization or othercompensation techniques. Second, it is difficult, if not impossible, forCVD to provide uniform coverage of trench sidewalls or complete fillingof holes and trenches.

To address these shortcomings, fabricators have developed atomic-layerdeposition (ALD), a special form of CVD that allows highly uniformformation of ultra-thin layers having thicknesses of one molecule orseveral atoms of the deposited material. Though similar to CVD in termsof equipment and process flow, ALD relies on adsorption of some of thereactants into exposed surfaces, and thus provides coverage and fill ofstructural features that are difficult, if not impossible, using CVD.

In recent years, researchers and engineers have made strides towardmaking ALD commercially viable for some applications. For example, oneteam of researchers reportedly optimized an ALD process for depositingan aluminum oxide (AlO_(x)) film in thin-film heads—devices used to readand write magnetic data. See, Paranjpe et al., Atomic Layer Depositionof AlO_(x) for Thin Film Head Gap Applications, Journal ofElectrochemical Society, 148 (9), pp. G465-G471 (2001), which isincorporated herein by reference.

However, the present inventors have recognized that the equipment andprocesses reported as optimal for thin-film head applications sufferfrom some limitations relative to use in fabricating integratedcircuits. For example, the reported process deposits material at theslow rate of less than one Angstrom per cycle, suggesting that more than50 cycles would be necessary to form a 50-Angstrom-thick layer.Moreover, the reported equipment uses a larger than desirable reactionchamber, which takes longer to fill up or pump out, and thus prolongsthe duration of each deposition cycle.

Accordingly, there is a need for better systems and methods ofatomic-layer deposition of aluminum oxides as well as other materialcompositions.

SUMMARY OF SELECTED EMBODIMENT(S)

To address these and/or other problems, the present inventor devised newsystems, methods, and apparatuses for atomic layer deposition. Oneexemplary atomic-layer deposition system, well suited for aluminum-oxidedepositions in integrated-circuit fabrication, includes an outerchamber, a substrate holder, and a unique gas-distribution fixture. Thefixture includes a gas-distribution surface having two sets of holes anda gas-confinement member that forms a wall around the holes. Inoperation, one set of holes dispenses an aluminum-carrying precursor andthe other dispenses an oxidizing agent gas, after the gas-confinementmember engages, or otherwise cooperates with the substrate holder toform an inner chamber within the outer chamber.

The inner chamber has a smaller volume than the outer chamber and thusconsumes less gas during the deposition process than would the outerchamber used alone. Also, the smaller chamber volume allows the exhaustsystem to pump the chamber more quickly, thus allowing shorter ALDcycles and potentially increasing rates of production.

These and other embodiments, aspects, advantages, and features of thepresent invention are set forth in part in the description and claimswhich follow, and in part will become apparent to those skilled in theart by reference to the following description of the invention andreferenced drawings or by practice of the invention. The aspects,advantages, and features of the invention are realized and attained bymeans of the instrumentalities, procedures, and combinationsparticularly pointed out in the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a side view of an exemplary deposition reactor according tothe invention;

FIG. 2 is a plan view of an exemplary gas-distribution fixture accordingto the invention; and

FIG. 3 is a flowchart showing an exemplary method according to theinvention.

DETAILED DESCRIPTION OF THE EXEMPLARY EMBODIMENTS

The following detailed description, which references and incorporatesthe above-identified figures, describes and illustrates one or morespecific embodiments of the invention. These embodiments, offered not tolimit but only to exemplify and teach the invention, are shown anddescribed in sufficient detail to enable those skilled in the art tomake and use the invention. Thus, where appropriate to avoid obscuringthe invention, the description may omit certain information known tothose of skill in the art.

FIG. 1 shows an exemplary atomic-layer-deposition system 100 whichincorporates teachings of the present invention. In particular, system100 includes a chamber 110, a wafer holder 120, a gas-distributionfixture (or showerhead) 130, a gas-supply system 140, and exhaust pumps150 and 160.

More particularly, chamber 110 includes respective top and bottom plates112 and 114 and a sidewall 116. In the exemplary embodiment, chamber 110is a cylindrical structure formed of stainless steel or glass. However,other embodiments use different structures and materials. Bottom plate114 includes an opening 114A. Extending through opening 114A is a stemportion 122 of wafer holder 120.

Wafer holder 120 also includes a support platform 124, one or moreheating elements 126, one or more temperature sensors 128, and an RFsource 129. Holder 120 (also called a chuck) raises and rotates manuallyor automatically via lift and rotation devices, and is coupled to apower supply and temperature control circuitry (all of which are notshown). Support platform 124 supports one or more substrates, wafers, orintegrated-circuit assemblies 200. Substrate 200 has an exemplary widthor diameter of about 30 centimeters and an exemplary thickness in therange of 850-1000 microns. (The term “substrate,” as used herein,encompasses a semiconductor wafer as well as structures having one ormore insulative, conductive, or semiconductive layers and materials.Thus, for example, the term embraces silicon-on-insulator,silicon-on-sapphire, and other advanced structures.)

Heating elements 126 and temperature sensors 128 are used for heatingsubstrates 200 to a desired temperature. Radio Frequency (RF) source129, for example, a 1.25-kilowatt-13.56-megahertz RF generator, is usedto generate and sustain a capacitively coupled plasma between the waferholder and gas-distribution fixture 130. (Some embodiments usegenerators with smaller or larger capacities.)

Fixture 130, positioned above wafer holder 120 and substrate 200,includes a gas-distribution member 132, a surface-projection (orgas-confinement) member 134, and gas inlets 136 and 137. In theexemplary embodiment, fixture 130 has three operating positions 138A,138B, and 138C relative support platform 124. Fixture 130 takesoperating position 138A, before and after depositions and operatingposition 138B during depositions. Position 138C is taken during a plasmaanneal to ensure stability of the plasma.

Gas-distribution member 132 includes main gas inputs 132A and 132B,gas-distribution channels 132D and 132F, and gas-distribution holes 132Eand 132G. Main gas inputs 132A and 132B feed respective gas-distributionchannels 132D and 132F, which in turn feed respective gas-distributionholes 132E and 132G. (Holes 132E and 132G are actually interleaved inthe exemplary embodiment, though shown simply in the figure as spatiallysegregated groups.) Holes 132D and 132F define a gas-distributionsurface 132C.

In the exemplary embodiment, holes 132D and 132F are substantiallycircular with a common diameter in the range of 15-20 microns;gas-distribution channels 132D and 132F have a common width in the rangeof 20-45 microns; and surface 132C is substantially planar and parallelto platform 124 of wafer holder 120. However, other embodiments useother surface forms as well as shapes and sizes of holes and channels.

Extending from gas-distribution surface 132C is surface-projectionmember (or collar) 134. Member 134 projects or extends from surface 132Ctoward support platform 124, defining a fixture cavity 134A. Theexemplary embodiment forms surface-projection member 134 from stainlesssteel as a uniform annular or circular wall or collar that projectsperpendicularly from surface 132C to define a right-cylindrical cavity.

However, other embodiments form member 134 to project at other anglesrelative surface 132C. For example, some form the projection at an acuteor obtuse angle, such as 45 or 135 degrees, and others form theprojection to peripherally define an oval, ellipse, triangle, square, orany desirable regular or irregular polygon. Thus, the present inventionencompasses a wide variety of projection shapes and configurations,indeed any projection shape that facilitates definition of an effectivecavity or gas-confinement volume in cooperation with wafer holder 120and/or substrate 200.

FIG. 2, a plan view, shows further details of the exemplary embodimentof gas-distribution fixture 130. In particular, the plan view shows notonly exemplary circular peripheries of gas-distribution member 132 andsurface-projection member 134, but also an exemplary interleaveddistribution pattern for holes 132E and 132G, and an exemplaryorthogonal arrangement of gas-distribution channels 132D and 132F.(Holes 132E are shown darkly shaded to distinguish them from holes 132G,which are cross-hatched.)

Other embodiments use other hole distribution patterns and channelarrangements. For example, some embodiments include random or concentrichole patterns and various channel geometries, including concentriccircles, rectangles, or other regular or irregular concentric polygons.Some embodiments may also dedicate various subsets of channels andcorresponding holes to different gases. For example, one embodimentprovides one set of holes and channels for approximately uniformdistribution of a gas or vapor, such as TMA precursor and argon carriergas mixture, and another set of holes and channels for approximatelyuniform distribution of a gas or vapor, such as a water-argon mixture.

Gas-distribution member 132 can be made in a number of ways. Oneexemplary method entails laminating several material layers, with eachlayer including holes and/or channels to effect distribution of thegases to the separate holes. If the layers are made of silicon, thematerial layers can be patterned and etched, for example, usingconventional photolithographic or micro-electro-mechanical systems(MEMS) technology, to form holes and channels. Dry-etching techniquesproduce small openings and channels, while wet etching produces largeropenings and channels. For further details, see, for example, M.Engelhardt, “Modern Application of Plasma Etching and Patterning inSilicon Process Technology,” Contrib. Plasma Physics, vol. 39, no. 5,pp. 473-478 (1999). Also see co-pending and co-assigned U.S. patentapplication Ser. No. 09/797,324 (docket 303.717US1 and 00-0264), whichwas filed on Mar. 1, 2001 and which is incorporated herein by reference.

The processed layers can then be bonded together with the holes andchannels in appropriate alignment using known wafer-bonding techniques.See, for example, G. Krauter et al., “Room Temperature Silicon WaferBonding with Ultra-Thin Polymer Films,” Advanced Materials, vol. 9, no.5, pp. 417-420 (1997); C. E. Hunt et al., “Direct Bonding ofMicromachined Silicon Wafers for Laser Diode Heat ExchangerApplications,” Journal of Micromechan. Microeng, vol. 1, pp. 152-156(1991); Zucker, O. et al., “Applications of oxygen plasma processing tosilicon direct bonding,” Sensors and Actuators, A. Physical, vol. 36,no. 3, pp. 227-231 (1993), which are all incorporated herein byreference. See also, co-pending and co-assigned U.S. patent applicationSer. No. 09/189,276 (dockets 303.534US1 and 97-1468) entitled “LowTemperature Silicon Wafer Bond Process with Bulk Material BondStrength,” which was filed Nov. 10, 1998 and which is also incorporatedherein by reference. The resulting bonded structure is then passivatedusing thermal oxidation for example.

For an alternative fixture structure and manufacturing method that canbe combined with those of the exemplary embodiment, see U.S. Pat. No.5,595,606, entitled “Shower Head and Film Forming Apparatus Using Same,which is incorporated herein by reference. In particular, one embodimentbased on this patent adds a projection or gas-confinement member to thereported showerhead structure.

FIG. 1 also shows that gas inlets 136 and 137, which feed respectiveholes 132E and 132G, are coupled to gas-supply system 140. Specifically,gas-supply system 140 includes gas lines 142 and 143, gas sources 144,145, and 146, and manual or automated mass-flow controllers 147, 148,and 149. Gas line or conduit 142, which includes one or more flexibleportions (not specifically shown), passes through an opening 116A inchamber sidewall 116 to connect with gas inlet 136. Gas sources 144 and145 are coupled respectively via mass-flow controllers 147 and 148 togas line 142. Gas line 143, which also includes one or more flexibleportions (not specifically shown), passes through an opening 116B inchamber sidewall 116 is coupled via mass-flow controller 149 to source146.

In the exemplary embodiment, which is tailored for aluminum oxidedeposition, source 144 provides a vapor-drawn aluminum precursor, suchas trimethylaluminum (TMA) with a vapor pressure of 11 Torr at roomtemperature; source 145 provides a carrier gas, such as argon; andsource 146 provides an oxidant, such as a water-argon mixture. Thewater-argon mixture can be implemented by bubbling an argon carrierthrough a water reservoir. Other embodiments use other aluminumprecursors, such as trisobutylaluminum (TIBA), dimethylaluminum hydride(DMAH), AlC₃, and other halogenated precursors and organometallicprecursors. Other types of oxidants include H₂O₂, O₂, O₃, N₂O. Thus, thepresent invention is not limited to specific aluminum precursors oroxidants.

System 100 also includes vacuum pumps 150 and 160. Vacuum pump 150 iscoupled to gas-distribution fixture 130 via a mass-flow controller 152and gas line 142. And, vacuum pump 160 is coupled to the interior ofchamber 110 via a line 162 and an opening 114B in chamber bottom plate114.

In general operation, system 100 functions, via manual or automaticcontrol, to move gas-distribution fixture 130 from operating position138A to position 138B, to introduce reactant gases from sources 145,146, and 147 through holes 132E and 132G in gas-distribution fixture 130onto substrate 200, and to deposit desired matter, such as an aluminumoxide, onto a substrate.

More particularly, FIG. 3 shows a flowchart 300 which illustrates anexemplary method of operating system 100. Flowchart 300 includes processblocks 302-320.

The exemplary method begins at block 302 with insertion of substrate 200onto wafer holder 120. Execution then proceeds to block 304.

In block 304, the system forms or closes an inner chamber aroundsubstrate 200, or at least a portion of substrate 200 targeted fordeposition. In the exemplary embodiment, this entails using a lever orother actuation mechanism (not shown) to move gas-distribution fixture130 from position 138A to position 138B or to move wafer holder 120 fromposition 138B to 138A. In either case, this movement placesgas-distribution surface 132C 10-20 millimeters from an upper mostsurface of substrate 200. In this exemplary position, a lower-mostsurface of surface-projection member 134 contacts the upper surface ofsupport platform 124, with the inner chamber bounded by gas-distributionsurface 132C, surface-projection member 134, and the upper surface ofsupport platform 124.

Other embodiments define the inner chamber in other ways. For example,some embodiments include a surface-projection member on support platform124 of wafer holder 120 to define a cavity analogous in structure and/orfunction to cavity 134A. In these embodiments, the surface-projectionmember takes the form of a vertical or slanted or curved wall, thatextends from support platform 124 and completely around substrate 200,and the gas-distribution fixture omits a surface-projection member.However, some embodiments include one or more surface-projection memberson the gas-distribution fixture and the on the support platform, withthe projection members on the fixture mating, engaging, or otherwisecooperating with those on the support platform to define a substantiallyor effectively closed chamber. In other words, the inner chamber neednot be completely closed, but only sufficiently closed to facilitate adesired deposition.

In block 306, after forming the inner chamber, the exemplary methodcontinues by establishing desired ambient conditions for the desireddeposition. This entails setting temperature and pressure conditionswithin chamber 110, including cavity 134A. To this end, the exemplaryembodiment operates heating element 126 to heat substrate 200 to adesired temperature, such as 150-200° C., and operating vacuum pump 150and/or pump 160 to establish a desired ambient pressure, such as 3.0Torr. Gas-distribution fixture 130 is held at a temperature 30-50° C.warmer than its surroundings. (However, other embodiments can maintainthe fixture at other relative operating temperatures.) Afterestablishing the desired ambient conditions, execution continues atblock 308.

Block 308 entails hydroxylating the surface of substrate 200 byintroducing an oxidant into the separate chamber. To this end, theexemplary embodiment shuts mass-flow controllers 147 and 148 andoperates mass-flow controller 149 to transfer an oxidant, such as awater in an argon carrier, from source 146 through gas line 143 andholes 132G into cavity 134A for a period, such as two seconds.

Notably, the inner chamber is smaller in volume than chamber 100 andthus requires less gas and less fill time to achieve desired chemicalconcentrations (assuming all other factors equal.) More precisely, theexemplary embodiment provides an inner chamber with an empty volume inthe range of 70 to 350 cubic centimeters, based on a 1-to-5 millimeterinner-chamber height and a fixture with a 30-centimeter diameter.Additionally, the number and arrangement of holes in the fixture as wellas the placement of the holes close to the substrate, for example withinfive millimeters of the substrate, promote normal gas incidence anduniform distribution of gases over the targeted portion of substrate200.

Block 310 entails purging or evacuating the inner chamber to reducewater concentration in the gas-distribution fixture and inner chamber totrace levels. To this end, the exemplary method initially drives a highflow of argon gas from source 145 through fixture 130 into the innerchamber and then draws the gas out of the inner chamber through thefixture via vacuum pump 150, defining a purge cycle of less than fiveseconds, for example three-four seconds. The present invention, however,is not believed to be limited to any particular purge-cycle duration.

Next, as block 312 shows, the exemplary method introduces an aluminumprecursor into the inner chamber through gas-distribution fixture 130.This entail operating mass-flow controllers 147 and 148 to respectivelyallow the flow of TMA and an argon carrier into fixture 130 via line 142for a period of time such as 0.5-2.0 seconds. During this period, theargon carries the TMA to the hydroxylated surface of the substrate,causing formation of an approximately 0.8 Angstrom (Å) monolayer ofaluminum oxide (AlO_(x)).

Block 314 entails purging or evacuating the inner chamber to reduceprecursor concentration in the gas-distribution fixture and innerchamber to trace levels. To this end, the exemplary method initiallydrives a flow of argon gas from source 145 through fixture 130 into theinner chamber and then draws the gas out of the inner chamber throughthe fixture via vacuum pump 150. Again, this purge cycle is expected toconsume less than five seconds.

At this point, as represented by a return path 315 back to block 304,blocks 304-314 can be repeated as many times as desired to achieve analuminum-oxide layer within roughly one Angstrom of virtually anydesired thickness from 5-10 Angstroms upwards. For semiconductorapplications, such as forming gate dielectrics, thicknesses in the rangeof 50-80 Angstroms could be used.

Block 316 entails annealing the substrate and deposited aluminum-oxidelayer to enhance the dielectric breakdown voltage of the layer. In theexemplary embodiment, this entails moving fixture 130 to operatingposition 138C (which establishes a substrate-to-fixture separation inthe range of 30-50 millimeters) and using RF source 129 to generate a250 Watt capacitively coupled plasma at 0.12 Torr in an argon-oxygenatmosphere (10 atom percent O₂) between the wafer holder. Someembodiments anneal after every monolayer to maximize dielectricbreakdown strength, and some anneal after each 25-50 Angstroms ofdeposited material thickness. Though various anneal times are feasible,the exemplary embodiment anneals for 10-15 seconds in high-temperatureenvironment. A return path 317 back to block 304 indicates that blocks304-316 can be repeated as many times as desired.

In block 318, the system opens the separate chamber. In the exemplaryembodiment, this entails automatically or manually movinggas-distribution fixture 130 to position 138A. Other embodiments,however, move the wafer holder or both the fixture and the wafer holder.Still other embodiments may use multipart collar or gas-confinementmembers which are moved laterally relative the wafer holder orgas-distribution fixture to open and close an inner chamber.

In block 320, substrate 200 is unloaded from chamber 110. Someembodiments remove the substrate manually, and others remove it using anautomated wafer transport system.

CONCLUSION

In furtherance of the art, the inventors have presented new systems,methods, and apparatuses for atomic-layer deposition. One exemplarysystem includes an outer chamber, a substrate holder, and a uniquegas-distribution fixture. The fixture engages, or otherwise cooperateswith the substrate holder to form an inner chamber within the outerchamber. Notably, the inner chamber not only consumes less gas duringdeposition to reduce deposition waste and cost, but also facilitatesrapid filling and purging to reduce deposition cycle times (with allother factors being equal.)

The embodiments described above are intended only to illustrate andteach one or more ways of practicing or implementing the presentinvention, not to restrict its breadth or scope. The actual scope of theinvention, which embraces all ways of practicing or implementing theinvention, is defined only by the following claims and theirequivalents.

1. An atomic-layer deposition system comprising: a chamber; and agas-distribution fixture in the chamber, the fixture including agas-distribution surface having a first plurality of holes and a secondplurality of holes and a gas-confinement member extending from thegas-distribution surface around the first and second plurality of holes,wherein the first and second pluralities of holes are isolated from eachother such that gases that flow into the first and second pluralities ofholes do not mix inside the gas-distribution fixture.
 2. Theatomic-layer deposition system of claim 1, wherein the gas-confinementmember surrounds all the holes.
 3. The atomic-layer deposition system ofclaim 1, wherein the gas-confinement member consists essentially of amaterial different from that of the gas-distribution surface.
 4. Theatomic-layer deposition system of claim 1, wherein the gas-distributionsurface is substantially planar and includes silicon and silicon oxide.5. The atomic-layer deposition system of claim 1, wherein theatomic-layer deposition system includes an RF source coupled to waferholder.
 6. The atomic-layer deposition system of claim 1, wherein theatomic-layer deposition system includes: a wafer holder having awafer-support surface confronting the gas-distribution surface; a firstsource to couple a precursor to the first plurality of holes in thegas-distribution fixture; and a second source to couple an oxidant tothe second plurality of holes in the gas-distribution fixture.
 7. Theatomic-layer deposition system of claim 6, wherein the gas-confinementmember extends perpendicularly from the gas-distribution surface towardthe wafer-support surface.
 8. The atomic-layer deposition system ofclaim 6, wherein the wafer-support surface is substantially parallel tothe gas-distribution surface.
 9. The atomic-layer deposition system ofclaim 6, wherein the first source includes trimethylaluminum as theprecursor and the second source includes water as the oxidant.
 10. Anatomic-layer deposition system comprising: a chamber; a gas-distributionfixture in the chamber, the fixture including: a gas-distribution memberincluding: a plurality of first channels and a plurality of secondchannels; and a gas-distribution surface having a plurality of firstholes and a plurality of second holes, with each of the first holes influid communication with at least one of the first channels and each ofthe second holes in fluid communication with at least one the secondchannels, the plurality of first holes isolated from the plurality ofsecond holes such that gases that flow into the plurality of first holesand the plurality of second holes do not mix inside the gas-distributionfixture; and a gas-confinement member within the first chamber andextending around the plurality of first holes and the plurality ofsecond holes; a wafer holder having a wafer-support surface confrontingthe first and second holes; a first source to couple a precursor to theplurality of first channels; and a second source to couple an oxidant tothe plurality of second holes.
 11. The atomic-layer deposition system ofclaim 10, wherein the gas-confinement member extends perpendicularlyrelative to the gas-distribution surface.
 12. The atomic-layerdeposition system of claim 10, wherein the gas-confinement membersurrounds all the holes.
 13. The atomic-layer deposition system of claim10, wherein the gas-confinement member consists essentially of amaterial different from that of the gas-distribution surface.
 14. Theatomic-layer deposition system of claim 10, wherein the gas-distributionsurface is substantially planar and includes silicon.
 15. Theatomic-layer deposition system of claim 10, wherein the first sourceincludes trimethylaluminum as the precursor and the second sourceincludes water as the oxidant.
 16. An atomic-layer deposition systemcomprising: a first chamber for confining gases; a second chamber withinthe first chamber for at least partially containing a substrate duringdeposition; and a gas-distribution fixture in the second chamber, thefixture including a gas-distribution surface having a first plurality ofholes and a second plurality of holes and a gas-confinement memberextending from the gas-distribution surface around the first and secondplurality of holes, wherein the first and second pluralities of holesare isolated from each other such that gases that flow into the firstand second pluralities of holes do not mix inside the gas-distributionfixture.
 17. The atomic-layer deposition system of claim 16, wherein thefirst chamber is a right cylindrical chamber.
 18. The atomic-layerdeposition system of claim 16, wherein the second chamber includes asurface of a substrate-support structure.
 19. The atomic-layerdeposition system of claim 16, wherein atomic-layer deposition systemincludes a supply essentially of trimethylaluminum coupled to the secondchamber and a supply essentially of water coupled to the second chamber.20. An atomic-layer deposition system comprising: a first chamber havingan interior sidewall; and a second chamber within the first chamber, thesecond chamber including: a gas-distribution fixture in the secondchamber including a gas-distribution member having a first plurality ofholes and a second plurality of holes that define a gas-distributionsurface, wherein the first and second pluralities of holes are isolatedfrom each other such that gases that flow into the first and secondpluralities of holes do not mix inside the gas-distribution fixture; agas-confinement surface at least partly encircling the plurality ofholes, the gas-confinement surface spaced from the interior sidewall ofthe first chamber and nonparallel to the gas-distribution surface; and awafer-support surface confronting the gas-distribution surface.
 21. Theatomic-layer deposition system of claim 20, wherein the gas-confinementsurface is substantially perpendicular to the gas-distribution surface.22. The atomic-layer deposition system of claim 20, wherein the wafersupport surface is substantially parallel to the gas-distributionsurface.
 23. The atomic-layer deposition system of claim 20, wherein thegas-confinement surface consists essentially of a material differentfrom that of the gas-distribution surface.
 24. The atomic-layerdeposition system of claim 20, wherein the gas-distribution surface issubstantially planar and includes silicon.
 25. The atomic-layerdeposition system of claim 20, wherein the atomic-layer depositionsystem includes: a first source to couple an aluminum precursor to thesecond chamber; and a second source to couple an oxidant to the secondchamber.
 26. An atomic-layer deposition system comprising: a firstchamber having an interior sidewall; a second chamber within the firstchamber, the second chamber including: a gas-distribution fixture in thesecond chamber including a gas-distribution member having a firstplurality of holes and a second plurality of holes that define agas-distribution surface, wherein the first and second pluralities ofholes are isolated from each other such that gases that flow into thefirst and second pluralities of holes do not mix inside thegas-distribution fixture; a gas-confinement wall at least partlyencircling the plurality of holes, the gas-confinement wall spaced fromthe interior sidewall of the first chamber and nonparallel to thegas-distribution surface; and a wafer-support surface confronting thegas-distribution surface; a first source to couple a precursor to thesecond chamber; and a second source to couple an oxidant to the secondchamber.
 27. The atomic-layer deposition system of claim 26, wherein thewafer-support surface contacts the gas-confinement wall.
 28. Theatomic-layer deposition system of claim 26, wherein the gas-confinementwall is substantially perpendicular to the gas-distribution surface andthe wafer-support surface.
 29. The atomic-layer deposition system ofclaim 26, wherein the wall has a uniform height measured from thegas-distribution surface.
 30. The atomic-layer deposition system ofclaim 26, wherein the wall consists essentially of a stainless steel.31. The atomic-layer deposition system of claim 26, wherein theatomic-layer deposition system includes a first plurality of channels influid communication with a first subset of the holes and secondplurality of channels in fluid communication with a second subset of theholes.
 32. The atomic-layer deposition system of claim 26, wherein thefirst source includes trimethylaluminum as the precursor and the secondsource includes water as the oxidant.